LY12CZ鋁合金極化腐蝕的聲發射研究
加入技術交流群
利用聲發射技術研究了LY12CZ鋁合金在3.5%NaCl溶液中的極化腐蝕行為。極化曲線和不同恒電位下極化的聲發射測量顯示，聲發射事件率與極化電流密度近似成線性關系，說明無論是陽極溶解還是鋁合金的陰極腐蝕都是重要的聲發射源。另外分別對恒電位-600mV陽極極化和-1500mV陰極極化下的聲發射事件進行了測試和分析。結果表明，無論是陽極極化還是陰極極化過程都存在兩種類型聲發射信號，不同的信號類型對應著不同的腐蝕過程和腐蝕機理。
ACOUSTIC EMISSION STUDY ON POLARIZATION CORROSION
OF LY12CZ ALUMINUM ALLOY
Hong Chang1,2 Enhou Han1 Jianqiu Wang1
（1 Environment Corrosion Center, Institute of Metal Research, Chinese Academy of Science, Shenyang 110016)
（2 Materials Science Engineering College, Shenyang Ligong University, Shenyang，110168）
Abstract: Polarization corrosion of LY12CZ aluminum alloy is studed using acoustic emission (AE) technology. Polarization curve and constant potential polarization experiments showed that AE events rate is linear to polarization current density. Anodic and cathodic polarization are both AE sources. Two types of AE signals are found both at －600mV (anodic) and at －1500mV (cathodic) constant potential polarization, but they are from different corrosion mechanisms.
Keywords：Aluminum alloy，Polarization corrosion，Acoustic emission[1]，從而為腐蝕過程和機制的分析提供依據。
[2]認為鋁在5%NaCl水溶液中腐蝕所產生的聲發射信號與析氫速度和電偶腐蝕存在直接關系，而且鉻酸鹽濃度的增加會降低聲發射強度，是因為鉻的增加阻礙了電偶腐蝕。Mansfeld[3,4]對Al2024在3.5%NaCl水溶液中的點蝕聲發射的研究表明聲發射事件率與點蝕中氫的析出有良好的對應關系。還有一些工作重點研究有氫氣產生的腐蝕反應導致的聲發射現象[5-7]。
2Cu）是主要強化相，基體上也有少量的S相（Al2CuMg）。
2，工作面用600-1500#耐水砂紙逐級打磨后，再用丙酮除油，蒸餾水反復沖洗，放于干燥器中干燥24小時后待用。干燥24小時足以使鋁合金的表面氧化膜穩定。其它溶液暴露區（II區）用丙烯酸酯涂覆。全部實驗在室溫下的3.5%NaCl水溶液中進行，帶寬為20-1000KHz的兩個寬帶傳感器（美國PAC公司出產的WD型）對稱分布于工作面兩側，與試件之間采用2211型硅油耦合劑耦合。聲發射測試采用PAC公司的4通道全數字DiSP聲發射系統，所有實驗參數都是通過事先的測試與試驗而選擇的較為合理的設置值。實驗中記錄了振鈴數、事件數、幅值、上升時間等信號參數，同時，也實時采集了信號波形，用于波形和頻譜分析。